FrictionalForceMicroscopy Phthalocyanine Gallium Hair PolymerBlend PS_PVAC InLiquid fluoroalkane PetruPoni BTO UnivOfMaryland PolyvinylAcetate Carbon Lanthanum_aluminate IISCBangalore Indent Yeditepe_University AEAPDES PvdfBead Polyaniline PrCurve bias_mode Polyvinylidene_fluoride India CrAu PatternedSapphireSubstrat Galfenol NUSNNI Magnetic InsulatorFilm AdhesionForce PinpointPFM SiliconCrystal Multiferroic_materials SiWafer
Report image
If you found this image unacceptable, please let us know. We will review your report and take action if we determine this image is really unacceptable.
Collagen film phase change by temp
Scanning Conditions
- System: NX10
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan