InLiquid Christmas Ni-FeAlloy Aluminum Multiferroic_materials Metal-organicComplex GlassTemp Optoelectronic PyroelectricDetector Friction Iron Alloy Pipette nanomechanical Polyimide CalciumHydroxyapatite dichalcogenide cannabis TiO2 fluoroaalkane membrane LiBattery ChemicalCompound HardDiskMedia LiIonBattery LiquidCrystal lithography polymeric_arrays PiezoelectricForceMicroscopy Zagreb Celebration Deposition TappingMode OrganicSemiconductor SSRM
Report image
If you found this image unacceptable, please let us know. We will review your report and take action if we determine this image is really unacceptable.
Collagen film phase change by temp
Scanning Conditions
- System: NX10
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan